Introduction of forged 6061-t6 aluminum
T6 is artificially aged after solution heat treatment. It is suitable for products that are no longer cold processed after solution heat treatment (straightening and leveling can be carried out, but the mechanical performance limit is not affected).
forged 6061-t6 aluminum has high strength, high hardness (up to HV90 degrees or more), good processing effect, and good oxidation effect. There are no trachoma pores and the flatness is better. Improve processing efficiency and reduce material costs. This will be the best choice for low price and high quality materials. The forged 6061-t6 aluminum series is made of aluminum, magnesium, and silicon alloys. It is a heat-treated corrosion-resistant alloy. The strength and corrosion resistance are relatively good, and the uniformity is good.
The chemical composition of forged 6061-t6 aluminum
Cu: 0.15-0.4 ãSi: 0.4-0.8ã ãFe: 0.7-,0.13 ãMn0.15-0.50ã ãMg: 0.8-1.2 ãZn: 0.25-0.50 ãCr: 0.04-0.35 ãTi: 0.15-0.63 ã They are four-digit magnesium Aluminum alloy with silicon as the main alloying element and Mg2Si phase as the strengthening phase.
Application of forged 6061-t6 aluminum
The main alloying elements of forged 6061-t6 aluminum are magnesium and silicon, which have medium strength, good corrosion resistance, weldability and good oxidation effect. It is widely used in various industrial structural parts that require a certain strength (85-110 degrees) and high corrosion resistance, such as the manufacture of trucks, tower buildings, ships, trams, railway vehicles, furniture mechanical parts, precision machining, molds, etc.
T6 is artificially aged after solution heat treatment. It is suitable for products that are no longer cold processed after solution heat treatment (straightening and leveling can be carried out, but the mechanical performance limit is not affected).
forged 6061-t6 aluminum has high strength, high hardness (up to HV90 degrees or more), good processing effect, and good oxidation effect. There are no trachoma pores and the flatness is better. Improve processing efficiency and reduce material costs. This will be the best choice for low price and high quality materials. The forged 6061-t6 aluminum series is made of aluminum, magnesium, and silicon alloys. It is a heat-treated corrosion-resistant alloy. The strength and corrosion resistance are relatively good, and the uniformity is good.
The chemical composition of forged 6061-t6 aluminum
Cu: 0.15-0.4 ãSi: 0.4-0.8ã ãFe: 0.7-,0.13 ãMn0.15-0.50ã ãMg: 0.8-1.2 ãZn: 0.25-0.50 ãCr: 0.04-0.35 ãTi: 0.15-0.63 ã They are four-digit magnesium Aluminum alloy with silicon as the main alloying element and Mg2Si phase as the strengthening phase.
Application of forged 6061-t6 aluminum
The main alloying elements of forged 6061-t6 aluminum are magnesium and silicon, which have medium strength, good corrosion resistance, weldability and good oxidation effect. It is widely used in various industrial structural parts that require a certain strength (85-110 degrees) and high corrosion resistance, such as the manufacture of trucks, tower buildings, ships, trams, railway vehicles, furniture mechanical parts, precision machining, molds, etc.