Specification introduction of Large forged aluminum rings
Alloy state: 5083 H112
Specification: φ2200mm x φ1920mm x 375mm
Introduction of mechanical properties:
Tensile strength: >300MPA
Yield strength: >150MPA
Elongation:> 15%
Chemical composition of Large forged aluminum rings
Al: margin
Si ï¼≤0.40
Cu: ≤0.10
Mg: 4.0ï½4.9
Zn: ≤0.25
Mn: 0.40ï½1.0
Ti ï¼≤0.15
Cr: 0.05ï½0.25
Fe: 0.000ï½0.400
Note: Single: ≤0.05; Total: ≤0.15
Application of Large forged aluminum rings
Large forged aluminum rings is used to produce the necessary fastening parts for the sealing of aviation, aerospace, military, and industrial equipment.
Alloy state: 5083 H112
Specification: φ2200mm x φ1920mm x 375mm
Introduction of mechanical properties:
Tensile strength: >300MPA
Yield strength: >150MPA
Elongation:> 15%
Chemical composition of Large forged aluminum rings
Al: margin
Si ï¼≤0.40
Cu: ≤0.10
Mg: 4.0ï½4.9
Zn: ≤0.25
Mn: 0.40ï½1.0
Ti ï¼≤0.15
Cr: 0.05ï½0.25
Fe: 0.000ï½0.400
Note: Single: ≤0.05; Total: ≤0.15
Application of Large forged aluminum rings
Large forged aluminum rings is used to produce the necessary fastening parts for the sealing of aviation, aerospace, military, and industrial equipment.