Introduction of 7050 T7451 aluminum forged discs rings
7050 T7451 aluminum forged discs rings is a heat treatable alloy with very high mechanical properties and high fracture toughness.
7050 T7451 aluminum forged discs rings is popular in aerospace industry. It has good stress resistance, corrosion cracking resistance and high strength at low temperature.
The temper of 7050 T7451 aluminum forged discs rings
7050-T6ã7050-T7451
Chemical composition of 7050 T7451 aluminum forged discs rings
Aluminum:Remainder
Chromium is less than 0.04.
Zirconium 0.08-0.15
Zinc 5.7 to 6.7
Silicon is less than 0.12
Iron 0.000-0.150
Manganese is less than 0.10.
Magnesium 1.9 to 2.6
Titanium is less than 0.06.
Copper 2 to 2.6
7050 T7451 aluminum forged discs rings application:
7050 T7451 aluminum forged rings are mainly used for fuselage frame, bulkhead and wing skin. Other applications include structural application and ship parts, military parts, high-speed revolving body, mobile equipment and high stress parts
7050 T7451 aluminum forged discs rings is a heat treatable alloy with very high mechanical properties and high fracture toughness.
7050 T7451 aluminum forged discs rings is popular in aerospace industry. It has good stress resistance, corrosion cracking resistance and high strength at low temperature.
The temper of 7050 T7451 aluminum forged discs rings
7050-T6ã7050-T7451
Chemical composition of 7050 T7451 aluminum forged discs rings
Aluminum:Remainder
Chromium is less than 0.04.
Zirconium 0.08-0.15
Zinc 5.7 to 6.7
Silicon is less than 0.12
Iron 0.000-0.150
Manganese is less than 0.10.
Magnesium 1.9 to 2.6
Titanium is less than 0.06.
Copper 2 to 2.6
7050 T7451 aluminum forged discs rings application:
7050 T7451 aluminum forged rings are mainly used for fuselage frame, bulkhead and wing skin. Other applications include structural application and ship parts, military parts, high-speed revolving body, mobile equipment and high stress parts