Heat treatment process and mechanical properties of 6061 T6 Forged Aluminum ring
The heat treatment process of 6061 T6 Forged Aluminum ring includes 1) quenching the forged ring, the quenching temperature is 520°C 550°C; 2) the aging treatment of the forging ring, the aging treatment temperature is 150°C 180 °C; the aging treatment time is 10 hours, and the aging treatment heating time is 10 12 hours.
Mechanical properties of 6061 T6 Forged Aluminum ring:
Tensile strength: >300MPA
Yield strength: >230MPA
Elongation:> 12%
Chemical composition of 6061 T6 Forged Aluminum ring
Silicon: 0.40-0.8
Iron: 0.7
Copper: 0.15-0.40
Manganese: 0.15
Magnesium: 0.8-1.2
Chromium: 0.04-0.35
Zinc: 0.25
Titanium: 0.15
Aluminum: margin
Other: Single: 0.05 Total: 0.15
The heat treatment process of 6061 T6 Forged Aluminum ring includes 1) quenching the forged ring, the quenching temperature is 520°C 550°C; 2) the aging treatment of the forging ring, the aging treatment temperature is 150°C 180 °C; the aging treatment time is 10 hours, and the aging treatment heating time is 10 12 hours.
Mechanical properties of 6061 T6 Forged Aluminum ring:
Tensile strength: >300MPA
Yield strength: >230MPA
Elongation:> 12%
Chemical composition of 6061 T6 Forged Aluminum ring
Silicon: 0.40-0.8
Iron: 0.7
Copper: 0.15-0.40
Manganese: 0.15
Magnesium: 0.8-1.2
Chromium: 0.04-0.35
Zinc: 0.25
Titanium: 0.15
Aluminum: margin
Other: Single: 0.05 Total: 0.15