2219 T6 T852 aluminum forged discs rings Introduction
2219 T6 T852 aluminum forged discs rings, American wrought aluminum and aluminum alloy. 2219 T6 T852 aluminum forged discs rings has poor corrosion resistance and good machining performance; it has poor brazing properties and is easy to arc welding and spot welding.
2219 T6 T852 aluminum forged discs rings is suitable for structural parts and high-strength welded parts working at high temperature 315 â
The Chemical Composition of 2219 T6 T852 aluminum forged discs rings
Si: 0.20
Fe: 0.30
Cu: 5.8 ~ 6.9
Mn: 0.20 ~ 0.40
Mg: 0.02
Zn: 0.10
Ti: 0.29 ~ 0.10
Zr: 0.10 ~ 0.25
V: 0.05 ~ 0.25
Other single: 0.05, 0.15 margin
The characteristics and application of 2219 T6 T852 aluminum forged discs rings
UNS A92219, ISO R209 AlCu6Mn; China GB 2219 (LY19)
The Processing temper of 2219 T6 T852 aluminum forged discs rings:
T6 T852, mechanical properties refer to YS / T 479-2005
2219 T6 T852 aluminum forged discs rings, American wrought aluminum and aluminum alloy. 2219 T6 T852 aluminum forged discs rings has poor corrosion resistance and good machining performance; it has poor brazing properties and is easy to arc welding and spot welding.
2219 T6 T852 aluminum forged discs rings is suitable for structural parts and high-strength welded parts working at high temperature 315 â
The Chemical Composition of 2219 T6 T852 aluminum forged discs rings
Si: 0.20
Fe: 0.30
Cu: 5.8 ~ 6.9
Mn: 0.20 ~ 0.40
Mg: 0.02
Zn: 0.10
Ti: 0.29 ~ 0.10
Zr: 0.10 ~ 0.25
V: 0.05 ~ 0.25
Other single: 0.05, 0.15 margin
The characteristics and application of 2219 T6 T852 aluminum forged discs rings
UNS A92219, ISO R209 AlCu6Mn; China GB 2219 (LY19)
The Processing temper of 2219 T6 T852 aluminum forged discs rings:
T6 T852, mechanical properties refer to YS / T 479-2005