2124 Forged Plate Block Bar Rings introduction
2124 Forged Plate Block Bar Rings are of American brand and China brand is 2A12. 2124 Forged Plate Block Bar Rings, density 2.73 g / cm & sup3; (0.098 lb / in & sup3;). 2124 Forged Plate Block Bar Rings is a typical duralumin alloy in aluminum copper magnesium system. Its composition is fair and its comprehensive function is good. This kind of alloy is produced in many countries, and the consumption of duralumin roof is the largest.
The features of 2124 Forged Plate Block Bar Rings
2124 Forged Plate Block Bar Rings are characterized by high strength and certain heat resistance, which can be used as working parts below 150 ° C. When the temperature is higher than 125 ° C, the strength of 2124 Forged Plate Block Bar Rings is higher than that of 7075 alloy. The forming function is better in the hot state, annealed state and new quenched state, and the heat treatment strengthening effect is obvious, but the heat treatment process is strict. It has poor corrosion resistance, but it can be effectively protected by covering with pure aluminum; it is easy to produce cracks during welding, but it can be welded or riveted with special technology
The chemical composition of 2124 Forged Plate Block Bar Rings
Silicon: 0.5%
Iron: 0.5%
Copper: 3.8-4.9:0.5%
Iron: 0.5%
Copper: 3.8-4.9
Manganese: 0.3-0.9
Magnesium: 1.2-1.8
Chromium: 0.10
Nickel:-
Zinc: 0.25
Titanium: 0.15
Others: 0.15
Aluminum: others
The application of 2124 Forged Plate Block Bar Rings
2124 Forged Plate Block Bar Rings are widely used in aircraft structures, rivets, truck hubs, propeller components and other structural parts.
2124 Forged Plate Block Bar Rings are of American brand and China brand is 2A12. 2124 Forged Plate Block Bar Rings, density 2.73 g / cm & sup3; (0.098 lb / in & sup3;). 2124 Forged Plate Block Bar Rings is a typical duralumin alloy in aluminum copper magnesium system. Its composition is fair and its comprehensive function is good. This kind of alloy is produced in many countries, and the consumption of duralumin roof is the largest.
The features of 2124 Forged Plate Block Bar Rings
2124 Forged Plate Block Bar Rings are characterized by high strength and certain heat resistance, which can be used as working parts below 150 ° C. When the temperature is higher than 125 ° C, the strength of 2124 Forged Plate Block Bar Rings is higher than that of 7075 alloy. The forming function is better in the hot state, annealed state and new quenched state, and the heat treatment strengthening effect is obvious, but the heat treatment process is strict. It has poor corrosion resistance, but it can be effectively protected by covering with pure aluminum; it is easy to produce cracks during welding, but it can be welded or riveted with special technology
The chemical composition of 2124 Forged Plate Block Bar Rings
Silicon: 0.5%
Iron: 0.5%
Copper: 3.8-4.9:0.5%
Iron: 0.5%
Copper: 3.8-4.9
Manganese: 0.3-0.9
Magnesium: 1.2-1.8
Chromium: 0.10
Nickel:-
Zinc: 0.25
Titanium: 0.15
Others: 0.15
Aluminum: others
The application of 2124 Forged Plate Block Bar Rings
2124 Forged Plate Block Bar Rings are widely used in aircraft structures, rivets, truck hubs, propeller components and other structural parts.