Introduction and specifications of 2618 T852 Aluminium forged discs
2618 T852 Aluminium forged discs is an Al-Cu-Mg-Ni-Fe alloy that can be strengthened by heat treatment. The alloy has high heat resistance, the use temperature is 200~250â, the hot and cold workability is good, and the welding performance is moderate.
Discs
Alloy: 2618 Temper: T852
Maximum weight ≤ 5T
Diameter ≤ 2500mm
Executive standard: GBn223, YS/T479, ASTM B247, AMS series standards
Available Temper: O, F, H112, T3, T4, T5, T6, T62, T652, T73, T74, T7452, T852, etc.
Chemical composition of 2618 T852 Aluminium forged discs
Si:0.10-0..25
Fe:0.9-1.3
Cu: 1.9-2.7
Mg:1.3-1.8
Ni:0.9-1.2
Zn: 0.10
Ti:0.04-0.10
Al: margin
Application of 2618 T852 Aluminium forged discs
The 2618 T852 Aluminium forged discs is suitable for manufacturing parts used at higher temperatures, such as turbochargers for automobiles.
2618 T852 Aluminium forged discs is an Al-Cu-Mg-Ni-Fe alloy that can be strengthened by heat treatment. The alloy has high heat resistance, the use temperature is 200~250â, the hot and cold workability is good, and the welding performance is moderate.
Discs
Alloy: 2618 Temper: T852
Maximum weight ≤ 5T
Diameter ≤ 2500mm
Executive standard: GBn223, YS/T479, ASTM B247, AMS series standards
Available Temper: O, F, H112, T3, T4, T5, T6, T62, T652, T73, T74, T7452, T852, etc.
Chemical composition of 2618 T852 Aluminium forged discs
Si:0.10-0..25
Fe:0.9-1.3
Cu: 1.9-2.7
Mg:1.3-1.8
Ni:0.9-1.2
Zn: 0.10
Ti:0.04-0.10
Al: margin
Application of 2618 T852 Aluminium forged discs
The 2618 T852 Aluminium forged discs is suitable for manufacturing parts used at higher temperatures, such as turbochargers for automobiles.